The effect of in-office bleaching agents on the Vickers hardness and surface topography of polished and unpolished CAD/CAM composite materials

Alamoush, Rasha A, Yang, Jiawei, Alhotan, Abdulaziz, Haider, Julfikar ORCID: https://orcid.org/0000-0001-7010-8285, Matinlinna, Jukka P and Elraggal, Alaaeldin (2023) The effect of in-office bleaching agents on the Vickers hardness and surface topography of polished and unpolished CAD/CAM composite materials. Scientific Reports, 13 (1). p. 15341. ISSN 2045-2322

Preview

Published Version Available under License Creative Commons Attribution. Download (5MB) | Preview

Abstract

In-office bleaching, using hydrogen peroxide, is effective to remove dental enamel stains. However, bleaching agents can deteriorate surface properties of CAD-CAM materials. This in vitro study aimed to investigate the effect of in-office bleaching agents on Vickers hardness and surface topography of polished and unpolished dental CAD-CAM composite materials (Grandio blocs, Lava Ultimate, BRILLIANT Crios, Cerasmart), and a polymer-infiltrated ceramic network block (Vita Enamic). The specimens were randomly divided into two groups: unpolished or polished. The micro-hardness and surface topography of each group were measured before bleaching, after a 60 min bleaching period, and 24-h and one-month post-bleaching. In-office bleaching significantly influenced the Vickers hardness of both the polished and unpolished CAD/CAM composite blocks, with Vita Enamic exhibiting the least hardness stability among all groups. Furthermore, in-office bleaching significantly influenced the surface roughness of unpolished CAD/CAM composite blocks. There was a significant difference in hardness reduction between the polished and unpolished specimens for most of the investigated materials at different time points. The bleaching did not influence the surface roughness of the investigated polished group, except for Vita Enamic and Lava Ultimate. However, it did influence the surface roughness of the investigated materials in the unpolished group.