The Effects of Incorporating Ag-Zn Zeolite on the Surface Roughness and Hardness of Heat and Cold Cure Acrylic Resins

Aljafery, Ali M, Al-Jubouri, Ola M, Wally, Zena J, Almusawi, Rajaa M, Abdulrudha, Noor H and Haider, Julfikar ORCID: https://orcid.org/0000-0001-7010-8285 (2022) The Effects of Incorporating Ag-Zn Zeolite on the Surface Roughness and Hardness of Heat and Cold Cure Acrylic Resins. Journal of Composites Science, 6 (3). p. 85.

Preview

Published Version Available under License Creative Commons Attribution. Download (4MB) | Preview

Abstract

One of the most widely used materials for the fabrication of prosthetic dental parts is acrylic resin. Its reasonable mechanical and physical properties make it a popular material for a wide range of dental applications. Recently, many attempts have been made to improve the mechanical and biological properties of this material, such as by adding fibres, nanoparticles, and nanotubes. The current study aimed to evaluate the effects of adding an antimicrobial agent, Ag-Zn zeolite, on the surface roughness and hardness of the denture base resins. Ag-Zn zeolite particles were chemically prepared and added at different concentrations (0.50 wt.% and 0.75 wt.%) to the heat cure (HC) and cold cure (CC) acrylic resins. Zeolite particles were characterized and confirmed using X-ray diffraction (XRD) and Energy-Dispersive X-ray Spectroscopy (EDX) attached with a Scanning Electron Microscope (SEM). Sixty disk shape specimens (40 mm diameter and 2 mm thickness) were fabricated from the HC and CC resins with and without the zeolite. All the specimens were divided into two main groups based on the acrylic resins, then each was subdivided into three groups (n = 10) according to the concentration of the Ag-Zn zeolite. A surface roughness and a hardness tester were used to measure the surface finish and hardness of the specimens. The analysed data showed that the surface roughness values significantly decreased when 0.50 wt.% and 0.75 wt.% zeolite were incorporated in the HC resin specimens compared to the control group. However, this reduction was not significant in the case of CC resin, while the surface hardness was significantly improved after incorporating 0.50 wt.% and 0.75 wt.% zeolite for both the CC and HC resins. Incorporating Ag-Zn zeolite with acrylic resin materials could be beneficial for improving their surface finish and resistance to surface damage as defined by the higher hardness.