    Thermoplastic Composites reinforced with Multi-layer Woven Jute Fabric: A Comparative Analysis

    Muhammad Sayem, Abu Sadat ORCID logoORCID: https://orcid.org/0000-0003-3034-7892, Haider, Julfikar ORCID logoORCID: https://orcid.org/0000-0001-7010-8285, Naveed, Bilal, Sayeed, MM Alamgir and Sashikumar, Sravanthi (2022) Thermoplastic Composites reinforced with Multi-layer Woven Jute Fabric: A Comparative Analysis. Advances in Materials and Processing Technologies, 8 (1). pp. 355-379. ISSN 2374-068X

    [img]
    Preview
    Accepted Version
    Download (5MB) | Preview

    Abstract

    Three commonly available thermoplastic matrices - High-density polyethylene (HDPE), polypropylene (PP) and nylon 6 – are reinforced with hessian jute fabric in multi-layer sequence to prepare composite laminates by compression moulding technique. The composite had a nominal fibre content of 18% in terms of weight and a nominal thickness of 6.5 mm. The mechanical and fracture behaviours of the resultant laminates are tested and compared. It was found that the Nylon-Jute composite exhibited the highest values of tensile strength, Young’s modulus, flexural strength, flexural modulus and hardness. On the other hand, HDPE-Jute composite showed relatively poor performance. Interestingly, the HDPE-Jute composite exhibited the highest impact strength and the Nylon-Jute composite was the poorest in this regard. The amount of water absorption by the composites from highest to the lowest was found in the following order: Nylon-Jute > HDPE-Jute > PP-Jute.

    Impact and Reach

    Statistics

    Activity Overview
    6 month trend
    294Downloads
    6 month trend
    222Hits

    Additional statistics for this dataset are available via IRStats2.

    Altmetric

    Repository staff only

    Edit record Edit record