    Tribological performance of graphite-like carbon films with varied thickness

    Shi, X, Liskiewicz, TW ORCID logoORCID: https://orcid.org/0000-0002-0866-814X, Beake, BD, Chen, J and Wang, C (2020) Tribological performance of graphite-like carbon films with varied thickness. Tribology International, 149. p. 105586. ISSN 0301-679X

    [img]
    Preview
    Accepted Version
    Available under License Creative Commons Attribution Non-commercial No Derivatives.

    Download (2MB) | Preview

    Abstract

    © 2019 Elsevier Ltd Graphite-like carbon (GLC) films with different thickness were deposited on 316 L stainless steel using closed field unbalanced magnetron sputtering system to investigate the influence of film thickness on the microstructure, mechanical and tribological properties. The results showed that the surface of the deposited films exhibited granular-like morphology, and the sp 2 content, surface roughness increase with the increase of film thickness, leading to the lower of hardness and higher of the internal stress. Both of the friction curves obtained by nano-tribological tests and fretting wear experiments revealed a three-stage evolution tendency with the same wear mechanism for the first two stages. The intermediate thick GLC film had the lowest specific wear rate, whilst the fretting fatigue life increased with film thickness.

    Impact and Reach

    Statistics

    Activity Overview
    6 month trend
    483Downloads
    6 month trend
    306Hits

    Additional statistics for this dataset are available via IRStats2.

    Altmetric

    Repository staff only

    Edit record Edit record